clear uv resin 3300,3301,3322,3305,3306,3325

uv plastic adhesive glue 3300,3301,3322,3305,3306,3325 Enhanced formulation flexibility. Anti-aging well MOQ:1KG

uv plastic adhesive glue 3300,3301,3322,3305,3306,3325

MOQ: 1KG

The product is uv curable glue that cures in 200 ~ 400nm wavelength ultraviolet ray. Mainly used in plastics and plastic, plastic and glass, plastic and metal, plastic and TPU adhesive and so on.Aimed at selfadhesive plastic handicraft industry, and the main bonding of plastic includs: PMMA (acrylic, plexiglass), PC, ABS, PVC, PS, PCB, TPU and kinds of thermoplastics.

Feature

· General products have a very broad scope application, plastic with a variety of materials have excellent adhesive bonding effect.

· Flexible formula, after curing it will not be stress cracking , low temperature, high temperature and humidity performance, Excellent.

· Curing quickly, few seconds can be positioned, one minute to reach the highest intensity, which greatly improves work efficiency.

· Completely transparent after curing, the product unchanged yellow  and  whitening for long timeCompared with the traditional instantaneous Adhesive bonding, with resistance to ring measurement, non-whitening, flexibility and good..

Specifications 

Test project	3300	3301	3322	3305	3306	3325
appearance	clear liquid	clear liquid	clear liquid	clear liquid	clear liquid	clear liquid
Viscosity mpa.s	55	250	1500	50	6500	2500
position time	6	6	2	4	2	2
Curing Energy mj/cm²	1500	1500	1500	1500	1500	1500
the tensile strength between acrylic and acrylic (MPa)	>14	>14	>14	>16	>12	>14
the tensile strength between acrylic and glass(MPa)	>14	>14	>15	>15	>13	>13
the tensile strengh between acrylic and metal (MPa_	>13	>13	>15	>15	>16	>13
Hardness(ShaoD)	>54	>55	55	55	60	80
the transparency of after curing	high transparency	high transparency	high transparency	high transparency	high transparency	high transparency
feature	Low-viscosity, low shrinkage, stress cracking does not appear	Universal, for a variety of plastics have a greater adhesion	Universal, for a variety of plastics have a greater adhesion	Low-viscosity, very high adhesion to plastic	have excellent adhesive between plastics with metal	have excellent adhesive between TPU and plasitic

The positioning time of the above that is under glass and glass bonding in 40-watt Philips intensity of 7.5 mW/cm2 uv light condition measured. 

the way of using 

First, clean the glass surface, dry the glass surface, and wait for the fully dried before dispensing.

Second, the glue uniform point in a glass surface, and the other glass conducts fit gently on the glue, forced to squeeze the glass and glue leveling bubble discharge, determine the position of bonding glue coverage and fixed-site well.

Third, use a cloth or paper towel to wipe around the overflow gel of the glass. Before this step, try to not let the glue exposure to ultraviolet light. Do not use with a damp cloth, wet paper, liquid (such as glass, water, water, alcohol, acetone and other solvents) to scrub the glass surrounding Resin before the glue completely cured.

Fourth, use a wavelength of 365 nm ultraviolet light to carve, until the layer has fully cured. Ultraviolet light irradiation is as close as possible to accelerate the curing speed glue.

Fifth, after ultraviolet radiation curing, you can resin the gel of the glass around curettage. 

Notes

1. The ideal thickness of bonding layer is 0.01-0.05mm, if too thin or too thick, it will be affected to the adhesion properties.

2. Ensure that the adhesive layer to absorb enough ultraviolet energy in order to achieve the best curing effect, or possibly to influence adhesion layer.

3. Not back and forth movement of the glass, otherwise easily led to layer whitish and bonding strength decreased.

4. Residual glue can not be pumped back into the original packaging, should be stored at sealed dark room temperature and without rendering children.

Packaging

250 g / bottle, 1 kg / bottle, 20 kg / barrel

clear uv resin 3300,3301,3322,3305,3306,3325